This spring-loaded pin, part number 0853-0-15-20-82-14-11-0, is designed for high-durability applications, offering between 100,000 and 1,000,000 cycles. It features a robust current rating of 9A with a 10C temperature rise and low contact resistance. The pin is built to withstand significant shock and vibration without electrical discontinuity, making it suitable for demanding environments. Packaged in bulk for efficient integration into manufacturing processes.
| Product Number | Description | Packaging | Durability | Current Rating | Temperature Rise | Contact Resistance | Operating Temperature Range | Vibration | Shock | Shell Plating | Inner Spring Plating | Shell Material |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 0853-0-15-20-82-14-11-0 | Spring-Loaded Pin | Bulk | 100,000 to 1,000,000 Cycles | 9A | 10C | 20 m Max | -55/+125C (discontinuous) | No Elect. Discontinuity > 1s @ 0-200 HZ, 10G | No Elect. Discontinuity > 1s @ 50 G | 20 " Gold over Nickel | 10 " Gold over Nickel | BRASS ALLOY 360 (per ASTM B 16) or BRASS ALLOY 385 (per ASTM B455) |
| Property | Value |
|---|---|
| Chemical Composition | Cu 63% (max), Pb 3.7% (max), Fe .35% (max), Zn remainder |
| Temper as machined | H02/H04 |
| Yield Strength | 25-45 ksi |
| Tensile strength | 57-80 ksi |
| Hardness as machined | 80-90 Rockwell B |
| Electrical conductivity | 26% IACS* |
| Melting point | 1000C/840C (liquidus/solidus) |
| Property | Value |
|---|---|
| Chemical Composition | Cu 60% (max), Pb 3.5% (max), Fe .35% (max), Zn remainder |
| Temper as machined | H02/H04 |
| Yield Strength | 16 ksi(min) |
| Tensile strength | 48 ksi(min) |
| Hardness as machined | 80-90 Rockwell B |
| Electrical conductivity | 28% IACS* |
| Melting point | 1000C/840C (liquidus/solidus) |